Magnetic tape and magnetic tape device

ABSTRACT

Provided is a magnetic tape in which the total thickness of a non-magnetic layer and a magnetic layer is equal to or smaller than 0.60 μm, the magnetic layer includes a timing-based servo pattern, the magnetic layer includes fatty acid ester, a full width at half maximum of spacing distribution measured by optical interferometry regarding the surface of the magnetic layer before performing vacuum heating with respect to the magnetic tape is greater than 0 nm and equal to or smaller than 7.0 nm, a full width at half maximum of spacing distribution measured after performing the vacuum heating is greater than 0 nm and equal to or smaller than 7.0 nm, and a difference between a spacing measured after performing the vacuum heating and a spacing measured before performing the vacuum heating is greater than 0 nm and equal to or smaller than 8.0 nm.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority under 35 U.S.C 119 to Japanese PatentApplication No. 2016-124942 filed on Jun. 23, 2016. The aboveapplication is hereby expressly incorporated by reference, in itsentirety.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates to a magnetic tape and a magnetic tapedevice.

2. Description of the Related Art

Magnetic recording media are divided into tape-shaped magnetic recordingmedia and disk-shaped magnetic recording media, and tape-shaped magneticrecording media, that is, magnetic tapes (hereinafter, also simplyreferred to as “tapes”) are mainly used for data storage such as databack-up or archive. The recording of information into magnetic tape isnormally performed by recording a magnetic signal on a data band of themagnetic tape. Accordingly, data tracks are formed in the data band.

An increase in recording capacity (high capacity) of the magnetic tapeis required in accordance with a great increase in information contentin recent years. As means for realizing high capacity, a technology ofdisposing the larger amount of data tracks in a width direction of themagnetic tape by narrowing the width of the data track to increaserecording density is used.

However, when the width of the data track is narrowed and the recordingand/or reproduction of magnetic signals is performed by allowing therunning of the magnetic tape in a magnetic tape device (normallyreferred to as a “drive”), it is difficult that a magnetic headcorrectly follows the data tracks in accordance with the position changeof the magnetic tape in the width direction, and errors may easily occurat the time of recording and/or reproduction. Thus, as means forpreventing occurrence of such errors, a system using a head trackingservo using a servo signal (hereinafter, referred to as a “servosystem”) has been recently proposed and practically used (for example,see U.S. Pat. No. 5,689,384A).

SUMMARY OF THE INVENTION

In a magnetic servo type servo system among the servo systems, a servopattern is formed in a magnetic layer of a magnetic tape, and this servopattern is magnetically read to perform head tracking. More specificdescription is as follows.

First, a servo head reads a servo pattern formed in a magnetic layer(that is, reproduces a servo signal). A position of a magnetic head ofthe magnetic tape in a width direction is controlled in accordance withvalues (will be described later specifically) obtained by reading theservo pattern. Accordingly, when running the magnetic tape in themagnetic tape device for recording and/or reproducing a magnetic signal(information), it is possible to increase an accuracy of the position ofthe magnetic head following the data track, even when the position ofthe magnetic tape is changed in the width direction with respect to themagnetic head. By doing so, it is possible to correctly recordinformation on the magnetic tape and/or correctly reproduce informationrecorded on the magnetic tape.

As the magnetic servo type servo system described above, a timing-basedservo type system is widely used in recent years. In a timing-basedservo type servo system (hereinafter, referred to as a “timing-basedservo system”), a plurality of servo patterns having two or moredifferent shapes are formed in a magnetic layer, and a position of aservo head is recognized by an interval of time when the servo head hasread the two servo patterns having different shapes and an interval oftime when the servo head has read two servo patterns having the sameshapes. The position of the magnetic head of the magnetic tape in thewidth direction is controlled based on the position of the servo headrecognized as described above.

Meanwhile, the magnetic tape is normally used to be accommodated andcirculated in a magnetic tape cartridge. In order to increase recordingcapacity for 1 reel of the magnetic tape cartridge, it is desired toincrease total length of the magnetic tape accommodated in 1 reel of themagnetic tape cartridge. In order to increase the recording capacity, itis necessary that the magnetic tape is thinned (hereinafter, referred toas “thinning”). As one method of thinning the magnetic tape, a method ofdecreasing the total thickness of a non-magnetic layer and a magneticlayer of a magnetic tape including the non-magnetic layer and themagnetic layer on a non-magnetic support in this order is used.

In consideration of these circumstances, the inventors have studied theapplication of a magnetic tape having a decreased total thickness of anon-magnetic layer and a magnetic layer to a timing-based servo system.However, in such studies, it was clear that, a phenomenon which was notknown in the related art occurred, in which an output of a servo signalreproduced by a servo head is decreased compared to that in an initialrunning stage (hereinafter, also referred to as an “output decrease of aservo signal”) occurs, when a head tracking is continuously performedwhile causing the magnetic tape to run in a timing-based servo system,in a magnetic tape having the total thickness of a non-magnetic layerand a magnetic layer equal to or smaller than 0.60 m. The outputdecrease of a servo signal causes a decrease in an accuracy of theposition of the magnetic head following the data track in thetiming-based servo system (hereinafter, referred to as a “headpositioning accuracy”). Therefore, it is necessary that the outputdecrease of a servo signal is prevented, in order to more correctlyrecord information to the magnetic tape and/or more correctly reproducethe information recorded in the magnetic tape by using the timing-basedservo system.

Therefore, an object of the invention is to prevent an output decreaseof a servo signal of a timing-based servo system, in a magnetic tapehaving the total thickness of a non-magnetic layer and a magnetic layerequal to or smaller than 0.60 m.

According to one aspect of the invention, there is provided a magnetictape comprising: a non-magnetic support; a non-magnetic layer includingnon-magnetic powder and a binder on the non-magnetic support; and amagnetic layer including ferromagnetic powder and a binder on thenon-magnetic layer, in which the total thickness of the non-magneticlayer and the magnetic layer is equal to or smaller than 0.60 μm, themagnetic layer includes a timing-based servo pattern, the magnetic layerincludes fatty acid ester, a full width at half maximum of spacingdistribution measured by optical interferometry regarding the surface ofthe magnetic layer before performing vacuum heating with respect to themagnetic tape (hereinafter, also referred to as “FWHM_(before)”) isgreater than 0 nm and equal to or smaller than 7.0 nm, a full width athalf maximum of spacing distribution measured by optical interferometryregarding the surface of the magnetic layer after performing the vacuumheating with respect to the magnetic tape (hereinafter, also referred toas “FWHM_(after)”) is greater than 0 nm and equal to or smaller than 7.0nm, and a difference (S_(after)−S_(before)) between a spacing S_(after)measured by optical interferometry regarding the surface of the magneticlayer after performing the vacuum heating with respect to the magnetictape and a spacing S_(before) measured by optical interferometryregarding the surface of the magnetic layer before performing the vacuumheating with respect to the magnetic tape (hereinafter, also simplyreferred to as a “difference (S_(after)−S_(before))”) is greater than 0nm and equal to or smaller than 8.0 nm.

The “timing-based servo pattern” of the invention and the specificationis a servo pattern with which the head tracking of the timing-basedservo system can be performed. The timing-based servo system is asdescribed above. The servo pattern with which the head tracking of thetiming-based servo system can be performed, is formed in the magneticlayer by a servo pattern recording head (also referred to as a “servowrite head”) as a plurality of servo patterns having two or moredifferent shapes. As an example, the plurality of servo patterns havingtwo or more different shapes are continuously disposed at regularintervals for each of the plurality of servo patterns having the sameshapes. As another example, different types of the servo patterns arealternately disposed. The same shapes of the servo patterns do not onlymean the completely same shape, and a shape error occurring due to adevice such as a servo write head or the like is allowed. The shapes ofthe servo pattern with which the head tracking of the timing-based servosystem can be performed and the disposition thereof in the magneticlayer are well known and specific aspect thereof will be describedlater. Hereinafter, the timing-based servo pattern is also simplyreferred to as a servo pattern. In the specification, as heads, a “servowrite head”, a “servo head”, and a “magnetic head” are disclosed. Theservo write head is a head which performs recording of a servo signal asdescribed above (that is, formation of a servo pattern). The servo headis a head which performs reproduction of the servo signal (that is,reading of the servo pattern), and the magnetic head is a head whichperforms recording and/or reproduction of information.

In the invention and the specification, the “vacuum heating” of themagnetic tape is performed by holding the magnetic tape in anenvironment of pressure of 200 Pa to 0.01 MPa and an atmospheretemperature of 70° C. to 90° C. for 24 hours.

In the invention and the specification, the spacing measured by opticalinterferometry regarding the surface of the magnetic layer of themagnetic tape is a value measured by the following method. In addition,in the invention and the specification, the “surface of the magneticlayer” of the magnetic tape is identical to the surface of the magnetictape on the magnetic layer side.

In a state where the magnetic tape and a transparent plate-shaped member(for example, glass plate or the like) are overlapped on each other sothat the surface of the magnetic layer of the magnetic tape faces thetransparent plate-shaped member, a pressing member is pressed againstthe side of the magnetic tape opposite to the magnetic layer side atpressure of 5.05×10⁴ N/m (0.5 atm). In this state, the surface of themagnetic layer of the magnetic tape is irradiated with light through thetransparent plate-shaped member (irradiation region: 150,000 to 200,000μm²), and a spacing (distance) between the surface of the magnetic layerof the magnetic tape and the surface of the transparent plate-shapedmember is acquired based on intensity (for example, contrast ofinterference fringe image) of interference light generated due to adifference in an optical path between reflected light from the surfaceof the magnetic layer of the magnetic tape and reflected light from thesurface of the transparent plate-shaped member on the magnetic tapeside. The light emitted here is not particularly limited. In a casewhere the emitted light is light having an emission wavelength over acomparatively wide wavelength range as white light including lighthaving a plurality of wavelengths, a member having a function ofselectively cutting light having a specific wavelength or a wavelengthother than wavelengths in a specific wavelength range, such as aninterference filter, is disposed between the transparent plate-shapedmember and a light reception unit which receives reflected light, andlight at some wavelengths or some wavelength ranges of the reflectedlight is selectively incident to the light reception unit. In a casewhere the light emitted is light (so-called monochromatic light) havinga single luminescence peak, the member described above may not be used.The wavelength of light incident to the light reception unit can be setto be in a range of 500 to 700 nm, for example. However, the wavelengthof light incident to the light reception unit is not limited to be inthe range described above. In addition, the transparent plate-shapedmember may be a member having transparency with which light emittedpasses, to the extent that the magnetic tape is irradiated with lightthrough this member and interference light is obtained.

The measurement described above can be performed by using a commerciallyavailable tape spacing analyzer (TSA) such as Tape Spacing Analyzermanufactured by MicroPhysics, Inc., for example. The spacing measurementof the Examples was performed by using Tape Spacing Analyzermanufactured by MicroPhysics, Inc.

In addition, the full width at half maximum of spacing distribution ofthe invention and the specification is a full width at half maximum(FWHM), when the interference fringe image obtained by the measurementof the spacing described above is divided into 300,000 points, a spacingof each point (distance between the surface of the magnetic layer of themagnetic tape and the surface of the transparent plate-shaped member onthe magnetic tape side) is acquired, this spacing is shown with ahistogram, and this histogram is fit with Gaussian distribution.

Further, the difference (S_(after)−S_(before)) is a value obtained bysubtracting a mode before the vacuum heating from a mode after thevacuum heating of the 300,000 points.

In one aspect, the total thickness of the non-magnetic layer and themagnetic layer is 0.20 μm to 0.60 μm.

In one aspect, the difference (S_(after)−S_(before)) is greater than 0nm and equal to or smaller than 7.0 nm.

In one aspect, the difference (S_(after)−S_(before)) is 2.0 nm to 7.0nm.

In one aspect, the FWHM_(before) is greater than 0 nm and equal to orsmaller than 5.0 nm.

In one aspect, the FWHM_(after) is greater than 0 nm and equal to orsmaller than 5.0 nm.

In one aspect, the magnetic layer includes a non-magnetic filler. Thenon-magnetic filler is identical to the non-magnetic powder. In theinvention and the specification, the non-magnetic powder means anaggregate of a plurality of non-magnetic particles. The aggregate notonly includes an aspect in which particles configuring the aggregatedirectly come into contact with each other, but also includes an aspectin which a binder and an additive is interposed between the particles. Aterm “particles” is also used for describing the powder. The sameapplies to various powder forms of the invention and the specificationsuch as the ferromagnetic powder and the like.

In one aspect, the non-magnetic filler is colloidal particles. In theinvention and the specification, the “colloidal particles” are particleswhich are not precipitated and dispersed to generate a colloidaldispersion, when 1 g of the particles are added to 100 mL of at leastone organic solvent of at least methyl ethyl ketone, cyclohexanone,toluene, or ethyl acetate, or a mixed solvent including two or morekinds of the solvents described above at an arbitrary mixing ratio.

In one aspect, the colloidal particles are silica colloidal particles.

According to another aspect of the invention, there is provided amagnetic tape device comprising: the magnetic tape described above; amagnetic head; and a servo head.

According to one aspect of the invention, it is possible to provide amagnetic tape in which the total thickness of a non-magnetic layer and amagnetic layer is equal to or smaller than 0.60 μm, a servo pattern isformed in a magnetic layer, and an output decrease of a servo signal ofa timing-based servo system is prevented, and a magnetic tape devicewhich records and/or reproduces a magnetic signal to the magnetic tape.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an example of disposition of data bands and servo bands.

FIG. 2 shows a servo pattern disposition example of a linear-tape-open(LTO) Ultrium format tape.

FIG. 3 is a schematic configuration diagram of a vibration impartingdevice used in the Examples.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Magnetic Tape

According to one aspect of the invention, there is provided a magnetictape including: a non-magnetic support; a non-magnetic layer includingnon-magnetic powder and a binder on the non-magnetic support; and amagnetic layer including ferromagnetic powder and a binder on thenon-magnetic layer, in which the total thickness of the non-magneticlayer and the magnetic layer is equal to or smaller than 0.60 μm, themagnetic layer includes a timing-based servo pattern, the magnetic layerincludes fatty acid ester, a full width at half maximum (FWHM_(before))of spacing distribution measured by optical interferometry regarding thesurface of the magnetic layer before performing vacuum heating withrespect to the magnetic tape is greater than 0 nm and equal to orsmaller than 7.0 nm, a full width at half maximum (FWHM_(after)) ofspacing distribution measured by optical interferometry regarding thesurface of the magnetic layer after performing the vacuum heating withrespect to the magnetic tape is greater than 0 nm and equal to orsmaller than 7.0 nm, and a difference (S_(after)−S_(before)) between aspacing S_(after) measured by optical interferometry regarding thesurface of the magnetic layer after performing the vacuum heating withrespect to the magnetic tape and a spacing S_(before) measured byoptical interferometry regarding the surface of the magnetic layerbefore performing the vacuum heating with respect to the magnetic tapeis greater than 0 nm and equal to or smaller than 8.0 nm.

Hereinafter, the magnetic tape described above will be described morespecifically. The following description contains surmise of theinventors. The invention is not limited by such surmise. In addition,hereinafter, the examples are described with reference to the drawings.However, the invention is not limited to such exemplified aspects.

Timing-Based Servo Pattern

The magnetic tape includes a timing-based servo pattern in the magneticlayer. The timing-based servo pattern is the servo pattern describedabove. In a magnetic tape used in a linear recording system which iswidely used as a recording system of the magnetic tape device, forexample, a plurality of regions (referred to as “servo bands”) whereservo patterns are formed are normally present in the magnetic layeralong a longitudinal direction of the magnetic tape. A region interposedbetween two servo bands is referred to as a data band. The recording ofmagnetic signals (information) is performed on the data band and aplurality of data tracks are formed in each data band along thelongitudinal direction.

FIG. 1 shows an example of disposition of data bands and servo bands. InFIG. 1, a plurality of servo bands 10 are disposed to be interposedbetween guide bands 12 in a magnetic layer of a magnetic tape 1. Aplurality of regions 11 each of which is interposed between two servobands are data bands. The servo pattern is a magnetized region and isformed by magnetizing a specific region of the magnetic layer by a servowrite head. The region magnetized by the servo write head (positionwhere a servo pattern is formed) is determined by standards. Forexample, in a LTO Ultrium format tape which is based on a localstandard, a plurality of servo patterns tilted in a tape width directionas shown in FIG. 2 are formed on a servo band when manufacturing amagnetic tape. Specifically, in FIG. 2, a servo frame SF on the servoband 10 is configured with a servo sub-frame 1 (SSF1) and a servosub-frame 2 (SSF2). The servo sub-frame 1 is configured with an A burst(in FIG. 2, reference numeral A) and a B burst (in FIG. 2, referencenumeral B). The A burst is configured with servo patterns A1 to A5 andthe B burst is configured with servo patterns B1 to B5. Meanwhile, theservo sub-frame 2 is configured with a C burst (in FIG. 2, referencenumeral C) and a D burst (in FIG. 2, reference numeral D). The C burstis configured with servo patterns C1 to C4 and the D burst is configuredwith servo patterns D1 to D4. Such 18 servo patterns are disposed in thesub-frames in the arrangement of 5, 5, 4, 4, as the sets of 5 servopatterns and 4 servo patterns, and are used for recognizing the servoframes. FIG. 2 shows one servo frame for description. However, inpractice, in a magnetic layer of the magnetic tape in which a headtracking is performed in a timing-based servo system, a plurality ofservo frames are disposed in each servo band in a running direction. InFIG. 2, an arrow shows the running direction. For example, a LTO Ultriumformat tape generally includes 5,000 or more servo frames per a tapelength of 1 m, in each servo band of the magnetic layer. The servo headsequentially reads the servo patterns in the plurality of servo frames,while coming into contact with and sliding on the surface of themagnetic layer of the running magnetic tape.

In the timing-based servo system, a position of a servo head isrecognized based on an interval of time when the servo head has read thetwo servo patterns (reproduced servo signals) having different shapesand an interval of time when the servo head has read two servo patternshaving the same shapes. The time interval is normally obtained as a timeinterval of a peak of a reproduced waveform of a servo signal. Forexample, in the aspect shown in FIG. 2, the servo pattern of the A burstand the servo pattern of the C burst are servo patterns having the sameshapes, and the servo pattern of the B burst and the servo pattern ofthe D burst are servo patterns having the same shapes. The servo patternof the A burst and the servo pattern of the C burst are servo patternshaving the shapes different from the shapes of the servo pattern of theB burst and the servo pattern of the D burst. An interval of the timewhen the two servo patterns having different shapes are read by theservo head is, for example, an interval between the time when any servopattern of the A burst is read and the time when any servo pattern ofthe B burst is read. An interval of the time when the two servo patternshaving the same shapes are read by the servo head is, for example, aninterval between the time when any servo pattern of the A burst is readand the time when any servo pattern of the C burst is read. Thetiming-based servo system is a system supposing that occurrence of adeviation of the time interval is due to a position change of themagnetic tape in the width direction, in a case where the time intervalis deviated from the set value. The set value is a time interval in acase where the magnetic tape runs without occurring the position changein the width direction. In the timing-based servo system, the magnetichead is moved in the width direction in accordance with a degree of thedeviation of the obtained time interval from the set value.Specifically, as the time interval is greatly deviated from the setvalue, the magnetic head is greatly moved in the width direction. Thispoint is applied to not only the aspect shown in FIG. 1 and FIG. 2, butalso to entire timing-based servo systems. When recording andreproducing magnetic signals (information) by the magnetic head bycausing the magnetic tape to run in the magnetic tape device using thetiming-based servo system, a decrease in output of a servo signal whilecontinuously reading the servo pattern (continuously reproducing theservo signal) by the servo head causes a decrease in a measurementaccuracy of the time interval. As a result, while the running iscontinuously performed, a head positioning accuracy is decreased. Inregards to this point, in the studies of the inventors, it was foundthat the output decrease of the servo signal significantly occurs in themagnetic tape having the total thickness of the non-magnetic layer andthe magnetic layer equal to or smaller than 0.60 μm. The inventors havethought that a main reason of the output decrease of the servo signal isattached materials attached to a servo write head, while a plurality ofservo patterns are sequentially formed in the magnetic layer while theservo write head comes into contact with and slide on the surface of themagnetic layer of the magnetic tape. The inventors have surmised that,as a result of deterioration of servo pattern forming ability of theservo write head due to the effect of the attached materials, a magneticforce of the servo pattern formed is gradually deteriorated, while theservo patterns are continuously formed. It is thought that in themagnetic layer having the servo patterns formed as described above, theoutput of a servo signal is decreased, while the servo patterns arecontinuously read by the servo head (servo signals are continuouslyreproduced). The inventors have surmised that, a reason of theoccurrence of such a phenomenon in the magnetic tape having the totalthickness of the non-magnetic layer and the magnetic layer equal to orsmaller than 0.60 m may be a contact state between the servo write headand the surface of the magnetic layer of the magnetic tape which isdifferent from that of the magnetic tape having the total thickness ofthe non-magnetic layer and the magnetic layer exceeding 0.60 m.

With respect to this, as a result of the intensive studies of theinventors, it was clear that the output decrease of the servo signal ofthe magnetic tape having the total thickness of the non-magnetic layerand the magnetic layer equal to or smaller than 0.60 μm can be preventedby setting the FWHM_(before), FWHM_(after), and the difference(S_(after)−S_(before)) to be in the ranges described above. The surmiseof the inventors regarding this point will be described in the following(1) and (2).

(1) When forming a servo pattern on the magnetic layer by the servowrite head, a projection existing on the surface of the magnetic layernormally comes into contact (so-called real contact) with the servowrite head, however, a part lower than the projection of the surface ofthe magnetic layer (hereinafter, referred to as a “base part”) does notcome into contact with the servo write head or has a low contactfrequency. The inventors have surmised that the spacing described aboveis a value which is an index of a distance between this base part andthe servo write head. However, it is thought that, when a lubricantincluded in the magnetic layer forms a liquid film on the surface of themagnetic layer, the liquid film is present between the base part and theservo write head, and thus, the spacing becomes narrow by the thicknessof the liquid film.

However, the lubricant is generally broadly divided into a fluidlubricant and a boundary lubricant. Fatty acid ester included in themagnetic layer of the magnetic tape is called as a component which canfunction as a fluid lubricant. It is considered that the fluid lubricantcan protect the surface of the magnetic layer by forming a liquid filmon a surface on the magnetic layer side. The inventors have surmisedthat the attached material which is attached to the servo write head andcauses a deterioration of servo pattern forming ability of the servowrite head is mainly a cut scrap of the surface of the magnetic layergenerated due to the contact with the servo write head. With respect tothis, the inventors have thought that, the presence of the liquid filmformed by fatty acid ester on the surface of the magnetic layer causesthe protection of the surface of the magnetic layer and the preventionof generation of cut scraps due to the cutting of the surface of themagnetic layer due to the contact with the servo write head. However, anexcessive amount of fatty acid ester present on the surface of themagnetic layer causes sticking due to the formation of a meniscus(liquid crosslinking) between the surface of the magnetic layer and theservo write head due to fatty acid ester, and accordingly, the servopattern forming ability of the servo write head is deteriorated.

In regards to this point, the inventors focused that fatty acid ester isa component having properties of volatilizing by vacuum heating, and adifference (S_(after)−S_(before)) of a spacing between a state after thevacuum heating (state in which a liquid film formed by fatty acid esteris volatilized and removed) and a state before the vacuum heating (statein which the liquid film formed by fatty acid ester is present) was usedas an index of a thickness of the liquid film formed on the surface ofthe magnetic layer by fatty acid ester. The inventors have surmised thatthe presence of the liquid film formed on the surface of the magneticlayer by fatty acid ester so that the value of the difference is greaterthan 0 nm and equal to or smaller than 8.0 nm, causes the prevention ofthe occurrence of sticking and prevention of the generation of cuttingscraps due to the cutting of the surface of the magnetic layer.

(2) A smaller value of the full width at half maximum of spacingdistribution means that a variation in the values of the spacingmeasured on each part of the surface of the magnetic layer is small. Asa result of the intensive studies, the inventors found that it iseffective to increase uniformity of a contact state between the surfaceof the magnetic layer and the servo write head by increasing uniformityof a height of projection present on the surface of the magnetic layerand increasing uniformity of a thickness of a liquid film formed byfatty acid ester, in order to prevent sticking between the surface ofthe magnetic layer and the servo write head and occurrence of cutting ofthe surface of the magnetic layer, when the servo write head comes intocontact with and slides on the surface of the magnetic layer.

In regards to this point, it is considered that the reason of thevariation in values of the spacing is a variation in height of theprojection of the surface of the magnetic layer and a variation in thethickness of the liquid film formed by fatty acid ester. The inventorshave surmised that the spacing distribution FWHM_(before) measuredbefore the vacuum heating, that is, in a state where the liquid filmformed on the surface of the magnetic layer by fatty acid ester ispresent, becomes great, as the variation in height of the projection andthe variation in the thickness of the liquid film formed by fatty acidester are great, and particularly, the spacing distributionFWHM_(before) is greatly affected by the variation in the thickness ofthe liquid film formed by fatty acid ester. In contrast, the inventorshave surmised that the spacing distribution FWHM_(after) measured afterthe vacuum heating, that is, in a state where the liquid film formed byfatty acid ester is removed from the surface of the magnetic layer,becomes great, as the variation in height of the projection is great.That is, the inventors have surmised that small spacing distributionsFWHM_(before) and FWHM_(after) mean a small variation in the thicknessof the liquid film formed on the surface of the magnetic layer by fattyacid ester and a small variation in height of the projection. It wasclear that it is possible to prevent the decrease of the output of theservo signals while continuously reading the servo pattern (continuouslyreproducing the servo signal) by the servo head, by increasing theuniformity of the height of the projection and the thickness of theliquid film formed by fatty acid ester so that the spacing distributionsFWHM_(before) and FWHM_(after) are greater than 0 nm and equal to orsmaller than 7.0 nm. The inventors have surmised that this is realizedby preventing the deterioration of the servo pattern forming ability ofthe servo write head, by preventing the sticking between the surface ofthe magnetic layer and the servo write head and preventing theoccurrence of cutting of the surface of the magnetic layer, when theservo write head comes into contact with and slide on the surface of themagnetic layer.

However, the above-mentioned description is merely a surmise of theinventors and the invention is not limited thereto.

Hereinafter, the magnetic tape will be described more specifically.

Spacing Distributions FWHM_(before) and FWHM_(after)

Both of the spacing distribution FWHM_(before) before the vacuum heatingand the spacing distribution FWHM_(after) after the vacuum heating whichare measured in the magnetic tape are greater than 0 nm and equal to orsmaller than 7.0 nm. The inventors have surmised that this pointcontributes the prevention of the output decrease of the servo signal ofthe timing-based servo system. From a viewpoint of further preventingthe output decrease of the servo signal of the timing-based servosystem, the FWHM_(before) and the FWHM_(after) are preferably equal toor smaller than 6.5 nm, more preferably equal to or smaller than 6.0 nm,even more preferably equal to or smaller than 5.5 nm, still morepreferably equal to or smaller than 5.0 nm, and still even morepreferably equal to or smaller than 4.5 nm. The FWHM_(before) and theFWHM_(after) can be, for example, equal to or greater than 0.5 nm, equalto or greater than 1.0 nm, equal to or greater than 2.0 nm, or equal toor greater than 3.0 nm. Meanwhile, from a viewpoint of preventing theoutput decrease of the servo signal in the timing-based servo system, itis preferable that the values thereof are small, and therefore, thevalues thereof may be smaller than the exemplified values.

The spacing distribution FWHM_(before) before the vacuum heating can bedecreased mainly by decreasing the variation in the thickness of theliquid film formed by fatty acid ester. An example of a specific methodwill be described later. Meanwhile, the spacing distributionFWHM_(after) after the vacuum heating can be decreased by decreasing thevariation in height of the projection of the surface of the magneticlayer. In order to perform the decreasing described above, it ispreferable that a presence state of the powder component included in themagnetic layer, for example, non-magnetic filler, which will bedescribed later specifically, in the magnetic layer is controlled. Anexample of a specific method will be described later.

Difference (S_(after)−S_(before))

The difference (S_(after)−S_(before)) of the spacings before and afterthe vacuum heating measured in the magnetic tape is greater than 0 nmand equal to or smaller than 8.0 nm. From a viewpoint of furtherpreventing the cutting of the surface of the magnetic layer coming intocontact with the servo write head, the difference (S_(after)−S_(before))is preferably equal to or greater than 0.1 nm, more preferably equal toor greater than 1.0 nm, even more preferably equal to or greater than1.5 nm, and still more preferably equal to or greater than 2.0 nm.Meanwhile, from a viewpoint of further preventing the sticking betweenthe servo write head and the surface of the magnetic layer, thedifference (S_(after)−S_(before)) is preferably equal to or smaller than7.5 nm, more preferably equal to or smaller than 7.0 nm, even morepreferably equal to or smaller than 6.0 nm, still more preferably equalto or smaller than 5.0 nm, further more preferably equal to or smallerthan 4.0 nm, still more preferably equal to or smaller than 3.5 nm, andstill even more preferably equal to or smaller than 3.0 nm. Thedifference (S_(after)−S_(before)) can be controlled by the amount offatty acid ester added to a magnetic layer forming composition. Inaddition, the difference (S_(after)−S_(before)) can also be controlledby the amount of fatty acid ester added to a non-magnetic layer formingcomposition. The non-magnetic layer can play a role of holding alubricant and supplying the lubricant to the magnetic layer, and this isbecause fatty acid ester included in the non-magnetic layer may be movedto the magnetic layer and present in the surface of the magnetic layer.

Magnetic Layer

Fatty Acid Ester

The magnetic tape includes fatty acid ester in the magnetic layer. Thefatty acid ester may be included alone as one type or two or more typesthereof may be included. Examples of fatty acid ester include esters oflauric acid, myristic acid, palmitic acid, stearic acid, oleic acid,linoleic acid, linolenic acid, behenic acid, erucic acid, and elaidicacid. Specific examples thereof include butyl myristate, butylpalmitate, butyl stearate (butyl stearate), neopentyl glycol dioleate,sorbitan monostearate, sorbitan distearate, sorbitan tristearate, oleyloleate, isocetyl stearate, isotridecyl stearate, octyl stearate,isooctyl stearate, amyl stearate, and butoxyethyl stearate.

The content of fatty acid ester of the magnetic layer formingcomposition is, for example, 0.1 to 10.0 parts by mass and is preferably1.0 to 7.0 parts by mass with respect to 100.0 parts by mass offerromagnetic powder. In a case of using two or more kinds of differentfatty acid esters as the fatty acid ester, the content thereof is thetotal content thereof. In the invention and the specification, the sameapplies to content of other components, unless otherwise noted. Inaddition, in the invention and the specification, a given component maybe used alone or used in combination of two or more kinds thereof,unless otherwise noted.

The content of fatty acid ester in the non-magnetic layer formingcomposition is, for example, 0 to 10.0 parts by mass and is preferably0.1 to 8.0 parts by mass with respect to 100.0 parts by mass ofnon-magnetic powder.

Other Lubricants

In the magnetic tape, lubricants other than fatty acid ester may bearbitrarily included in the magnetic layer and/or the non-magneticlayer. As described above, the lubricant included in the non-magneticlayer may be moved to the magnetic layer and present in the surface ofthe magnetic layer. As the lubricant which may be arbitrarily included,fatty acid can be used. In addition, fatty acid amide and the like canalso be used. Fatty acid ester is called a component which can functionas a fluid lubricant, whereas fatty acid and fatty acid amide are calledas a component which can function as a boundary lubricant. It isconsidered that the boundary lubricant is a lubricant which can beattached to a surface of powder (for example, ferromagnetic powder) andform a rigid lubricant film to decrease contact friction.

Examples of fatty acid include lauric acid, myristic acid, palmiticacid, stearic acid, oleic acid, linoleic acid, linolenic acid, behenicacid, erucic acid, and elaidic acid, and stearic acid, myristic acid,and palmitic acid are preferable, and stearic acid is more preferable.Fatty acid may be included in the magnetic layer in a state of salt suchas metal salt.

As fatty acid amide, amide of various fatty acid described above isused, and examples thereof include lauric acid amide, myristic acidamide, palmitic acid amide, and stearic acid amide.

Regarding fatty acid and a derivative of fatty acid (amide and ester), apart derived from fatty acid of the fatty acid derivative preferably hasa structure which is the same as or similar to that of fatty acid usedin combination. As an example, in a case of using fatty acid and stearicacid, it is preferable to use stearic acid ester and/or stearic acidamide.

The content of fatty acid of the magnetic layer forming composition is,for example, 0 to 10.0 parts by mass, preferably 0.1 to 10.0 parts bymass, and more preferably 1.0 to 7.0 parts by mass, with respect to100.0 parts by mass of the ferromagnetic powder. The content of fattyacid amide of the magnetic layer forming composition is, for example, 0to 3.0 parts by mass, preferably 0 to 2.0 parts by mass, and morepreferably 0 to 1.0 part by mass with respect to 100.0 parts by mass ofthe ferromagnetic powder.

In addition, the content of fatty acid of the non-magnetic layer formingcomposition is, for example, 0 to 10.0 parts by mass, preferably 1.0 to10.0 parts by mass, and more preferably 1.0 to 7.0 parts by mass withrespect to 100.0 parts by mass of the non-magnetic powder. The contentof fatty acid amide of the non-magnetic layer forming composition is,for example, 0 to 3.0 parts by mass and preferably 0 to 1.0 part by masswith respect to 100.0 parts by mass of the non-magnetic powder.

Ferromagnetic Powder

As the ferromagnetic powder included in the magnetic layer,ferromagnetic powder normally used in the magnetic layer of variousmagnetic recording media can be used. It is preferable to useferromagnetic powder having a small average particle size, from aviewpoint of improvement of recording density of the magnetic tape. Fromthis viewpoint, ferromagnetic powder having an average particle sizeequal to or smaller than 50 nm is preferably used as the ferromagneticpowder. Meanwhile, the average particle size of the ferromagnetic powderis preferably equal to or greater than 10 nm, from a viewpoint ofstability of magnetization.

As a preferred specific example of the ferromagnetic powder,ferromagnetic hexagonal ferrite powder can be used. An average particlesize of the ferromagnetic hexagonal ferrite powder (average platediameter) is preferably 10 nm to 50 nm and more preferably 20 nm to 50nm, from a viewpoint of improvement of recording density and stabilityof magnetization. For details of the ferromagnetic hexagonal ferritepowder, descriptions disclosed in paragraphs 0012 to 0030 ofJP2011-225417A, paragraphs 0134 to 0136 of JP2011-216149A, andparagraphs 0013 to 0030 of JP2012-204726A can be referred to, forexample.

As a preferred specific example of the ferromagnetic powder,ferromagnetic metal powder can also be used. An average particle size(average long axis length) of the ferromagnetic metal powder ispreferably 10 nm to 50 nm and more preferably 20 nm to 50 nm, from aviewpoint of improvement of recording density and stability ofmagnetization. For details of the ferromagnetic metal powder,descriptions disclosed in paragraphs 0137 to 0141 of JP2011-216149A andparagraphs 0009 to 0023 of JP2005-251351A can be referred to, forexample.

In the invention and the specification, unless otherwise noted, anaverage particle sizes of various powders such as ferromagnetic powderis a value measured by the following method with a transmission electronmicroscope.

The powder is imaged at a magnification ratio of 100,000 with atransmission electron microscope, the image is printed on printing paperso that the total magnification of 500,000 to obtain an image ofparticles configuring the powder. A target particle is selected from theobtained image of particles, an outline of the particle is traced with adigitizer, and a size of the particle (primary particle) is measured.The primary particle is an independent particle which is not aggregated.

The measurement described above is performed regarding 500 particlesarbitrarily extracted. An arithmetical mean of the particle size of 500particles obtained as described above is an average particle size of thepowder. As the transmission electron microscope, a transmission electronmicroscope H-9000 manufactured by Hitachi, Ltd. can be used, forexample. In addition, the measurement of the particle size can beperformed by well-known image analysis software, for example, imageanalysis software KS-400 manufactured by Carl Zeiss. The averageparticle size shown in Examples which will be described later ismeasured by using transmission electron microscope H-9000 manufacturedby Hitachi, Ltd. as the transmission electron microscope, and imageanalysis software KS-400 manufactured by Carl Zeiss as the imageanalysis software, unless otherwise noted.

As a method of collecting a sample powder from the magnetic tape inorder to measure the particle size, a method disclosed in a paragraph of0015 of JP2011-48878A can be used, for example.

In the invention and the specification, unless otherwise noted, (1) in acase where the shape of the particle observed in the particle imagedescribed above is a needle shape, a fusiform shape, or a columnar shape(here, a height is greater than a maximum long diameter of a bottomsurface), the size (particle size) of the particles configuring thepowder is shown as a length of a long axis configuring the particle,that is, a long axis length, (2) in a case where the shape of theparticle is a planar shape or a columnar shape (here, a thickness or aheight is smaller than a maximum long diameter of a plate surface or abottom surface), the particle size is shown as a maximum long diameterof the plate surface or the bottom surface, and (3) in a case where theshape of the particle is a sphere shape, a polyhedron shape, or anunspecified shape, and the long axis configuring the particles cannot bespecified from the shape, the particle size is shown as an equivalentcircle diameter. The equivalent circle diameter is a value obtained by acircle projection method.

In addition, regarding an average acicular ratio of the powder, a lengthof a short axis, that is, a short axis length of the particles ismeasured in the measurement described above, a value of (long axislength/short axis length) of each particle is obtained, and anarithmetical mean of the values obtained regarding 500 particles iscalculated. Here, unless otherwise noted, in a case of (1), the shortaxis length as the definition of the particle size is a length of ashort axis configuring the particle, in a case of (2), the short axislength is a thickness or a height, and in a case of (3), the long axisand the short axis are not distinguished, thus, the value of (long axislength/short axis length) is assumed as 1, for convenience.

In addition, unless otherwise noted, in a case where the shape of theparticle is specified, for example, in a case of definition of theparticle size (1), the average particle size is an average long axislength, in a case of the definition (2), the average particle size is anaverage plate diameter, and an average plate ratio is an arithmeticalmean of (maximum long diameter/thickness or height). In a case of thedefinition (3), the average particle size is an average diameter (alsoreferred to as an average particle diameter).

The content (filling percentage) of the ferromagnetic powder of themagnetic layer is preferably in a range of 50 to 90 mass % and morepreferably in a range of 60 to 90 mass %. The components other than theferromagnetic powder of the magnetic layer are at least a binder andfatty acid ester, and one or more kinds of additives may be furtherarbitrarily included. A high filling percentage of the ferromagneticpowder in the magnetic layer is preferable from a viewpoint ofimprovement recording density.

Binder

The magnetic tape includes a binder in the magnetic layer together withthe ferromagnetic powder and fatty acid ester. The binder is one or morekinds of resin. As the binder, a resin selected from a polyurethaneresin, a polyester resin, a polyamide resin, a vinyl chloride resin, anacrylic resin obtained by copolymerizing styrene, acrylonitrile, ormethyl methacrylate, a cellulose resin such as nitrocellulose, an epoxyresin, a phenoxy resin, and a polyvinylalkylal resin such as polyvinylacetal or polyvinyl butyral can be used alone or a plurality of resinscan be mixed with each other to be used. Among these, a polyurethaneresin, an acrylic resin, a cellulose resin, and a vinyl chloride resinare preferable. These resins may be a homopolymer or a copolymer. Theseresins can be used as the binder even in the non-magnetic layer and/or aback coating layer which will be described later. For the binderdescribed above, description disclosed in paragraphs 0028 to 0031 ofJP2010-24113A can be referred to. In addition, the binder may be aradiation curable resin such as an electron beam-curable resin. For theradiation curable resin, descriptions disclosed in paragraphs 0044 and0045 of JP2011-48878A can be referred to.

In addition, a curing agent can be used together with a resin which canbe used as the binder. The curing agent is a compound including at leastone and preferably two or more crosslinking functional groups in onemolecule. As the curing agent, polyisocyanate is suitable. For thedetails of polyisocyanate, descriptions disclosed in paragraphs 0124 and0125 of JP2011-216149A can be referred to. The amount of the curingagent used can be, for example, 0 to 80.0 parts by mass with respect to100.0 parts by mass of the binder, and is preferably 50.0 to 80.0 partsby mass, from a viewpoint of improvement of strength of each layer suchas the magnetic layer.

Other Components

Additives can be added to the magnetic layer, if necessary. It ispreferable that the magnetic layer includes one or more kinds of thenon-magnetic filler. As the non-magnetic filler, a non-magnetic filler(hereinafter, also referred to as a “projection formation agent”) whichis added for controlling the projection of the surface of the magneticlayer and a non-magnetic filler which is added as an abrasive impartingabrasive properties to the surface of the magnetic layer are mainlyused. The magnetic layer preferably includes at least the projectionformation agent and more preferably includes the projection formationagent and the abrasive.

The non-magnetic filler which can function as the projection formationagent may be inorganic powder or organic powder, and is preferablyinorganic powder. In addition, carbon black is also preferable. Anaverage particle size (average primary particle size) of carbon black ispreferably equal to or greater than 20 nm and more preferably equal toor greater than 30 nm. In addition, the average particle size of carbonblack is preferably equal to or smaller than 150 nm and more preferablyequal to or smaller than 100 nm.

Examples of the inorganic powder include powder of metal oxide, metalcarbonate, metal sulfate, metal nitride, metal carbide, and metalsulfide, and specific examples thereof include powder of inorganicsubstances such as α-alumina, β-alumina, γ-alumina, θ-alumina, siliconoxide such as silicon dioxide, silicon carbide, chromium oxide, ceriumoxide, α-iron oxide, goethite, corundum, silicon nitride, titaniumcarbide, titanium dioxide, tin oxide, magnesium oxide, tungsten oxide,zirconium oxide, boron nitride, zinc oxide, calcium carbonate, calciumsulfate, barium sulfate, and molybdenum disulfide, or compositeinorganic substances including two or more kinds thereof. The inorganicoxide powder is more preferable and silicon oxide powder is even morepreferable.

The non-magnetic filler which can function as a projection formationagent preferably has uniformity of the particle size, from a viewpointof further improving electromagnetic conversion characteristics. From aviewpoint of availability of particles having high uniformity of theparticle size, the non-magnetic filler is preferably colloidalparticles. When the non-magnetic filler used in the formation of themagnetic layer can be available, it is possible to determine whether ornot the non-magnetic filler included in the magnetic layer is colloidalparticles, by evaluating whether or not such a non-magnetic filler hasproperties which are the properties of the colloidal particles describedabove. Alternatively, the determination can be also performed byevaluating whether or not the non-magnetic filler extracted from themagnetic layer has properties which are the properties of the colloidalparticles described above. The extraction of the non-magnetic fillerfrom the magnetic layer can be performed by the following method, forexample.

1. 1 g of the magnetic layer is scraped off. The scraping can beperformed, for example, by a razor blade.

2. A magnetic layer sample obtained by the scraping is put in a vesselsuch as an eggplant flask and 100 ml of tetrahydrofuran is added intothis vessel. Examples of tetrahydrofuran include commercially availabletetrahydrofuran to which a stabilizer is added and commerciallyavailable tetrahydrofuran to which a stabilizer is not added. Here, thecommercially available tetrahydrofuran to which a stabilizer is notadded is used. The same applies to tetrahydrofuran used in washingdescribed hereinafter.

3. A circulation tube is attached to the vessel and heated in a waterbath at a water temperature of 60° C. for 90 minutes. After filteringthe content in the heated vessel with a filter paper, the solid contentremaining on the filter paper is washed with tetrahydrofuran severaltimes, and the washed solid content is moved to a vessel such as abeaker. A 4 N (4 mol/L) hydrochloric acid aqueous solution is added intothis vessel and a residue remaining without being dissolved is extractedby filtering. As a filter, a filter having a hole diameter smaller than0.05 μm is used. For example, a membrane filter used for chromatographyanalysis (for example, MF Millipore manufactured by Merck MilliporeCorporation) can be used. The residue extracted by the filtering iswashed with pure water several times and dried.

Ferromagnetic powder and organic matters (binder and the like) aredissolved by the operation described above, and a non-magnetic filler iscollected as a residue.

By performing the steps described above, the non-magnetic filler can beextracted from the magnetic layer. In a case where a plurality of kindsof non-magnetic fillers are included in the non-magnetic fillerextracted as described above, the plurality of kinds of non-magneticfillers can be divided depending on differences of density.

As preferred colloidal particles, inorganic oxide colloidal particlescan be used. As the inorganic oxide colloidal particles, colloidalparticles of inorganic oxide described above can be used, and compositeinorganic oxide colloidal particles such as SiO₂.Al₂O₃, SiO₂.B₂O₃,TiO₂.CeO₂, SnO₂.Sb₂O₃, SiO₂.Al₂O₃.TiO₂, and TiO₂.CeO₂.SiO₂. Theinorganic oxide colloidal particles such as SiO₂, Al₂O₃, TiO₂, ZrO₂, andFe₂O₃ are preferable and silica colloidal particles (colloidal silica)is particularly preferable. Meanwhile, typical colloidal particles havea hydrophilic surface, and thus, the colloidal particles are suitablefor manufacturing a colloidal solution using water as a dispersionmedium. For example, colloidal silica obtained by a general synthesismethod has a surface covered with polarized oxygen atoms (O²⁻), andthus, colloidal silica adsorbs water in water, forms a hydroxyl group,and is stabilized. However, these particles are hardly present in acolloidal state, in an organic solvent normally used in the magneticlayer forming composition. With respect to this, the colloidal particlesof the invention and the specification are particles which are notprecipitated but are dispersed to cause a colloidal dispersion, when 1 gthereof is added with respect to 100 mL of the organic solvent describedabove. Such colloidal particles can be prepared by a well-known methodof hydrophobing the surface by surface treatment. For details of suchhydrophobization treatment, descriptions disclosed in JP1993-269365A(JP-H05-269365A), JP1993-287213A (JP-H05-287213A), and JP2007-63117A arereferred to.

As a manufacturing method of the silica colloidal particles (colloidalsilica) which are preferred colloidal particles, two kinds of methodssuch as a water glass method and a sol-gel method are generally known.The water glass method is a method of using silica soda (sodiumsilicate, so-called water glass) as a raw material, performing ionexchange with respect to this to generate an active silica, and causingparticle growth. Meanwhile, the sol-gel method is a method of usingtetraalkoxysilane as a raw material, and performing hydrolysis under abasic catalyst and causing particle growth at the same time. In a caseof using the silica colloidal particles as the non-magnetic filler, thesilica colloidal particles may be manufactured by any manufacturingmethod described above.

An average particle size of the non-magnetic filler which may functionas a projection formation agent is preferably in a range of 50 to 200nm, and more preferably in a range of 50 to 150 nm.

The content of the non-magnetic filler which may function as aprojection formation agent in the magnetic layer is preferably 1.0 to4.0 parts by mass and more preferably 1.5 to 3.5 parts by mass withrespect to 100.0 parts by mass of the ferromagnetic powder.

Meanwhile, the non-magnetic filler which may function as an abrasive maybe inorganic powder or organic powder, and the inorganic powder ispreferable. Examples of the non-magnetic powder which may function as anabrasive include powders of alumina (Al₂O₃), silicon carbide, boroncarbide (B₄C), SiO₂, TiC chromium oxide (Cr₂O₃), cerium oxide, zirconiumoxide (ZrO₂), iron oxide, diamond, and the like which are materialsnormally used as the abrasive of the magnetic layer, and among these,alumina powder such as α-alumina and silicon carbide powder arepreferable. The content of the non-magnetic filler which may function asan abrasive in the magnetic layer is preferably in a range of 1.0 to20.0 parts by mass, more preferably in a range of 3.0 to 15.0 parts bymass, and even more preferably in a range of 4.0 to 10.0 parts by masswith respect to 100.0 parts by mass of the ferromagnetic powder. Theaverage particle size of the non-magnetic filler which may function asan abrasive is, for example, in a range of 30 to 300 nm and preferablyin a range of 50 to 200 nm.

An arbitrary amount of one or more kinds of various additives such as adispersing agent, a dispersing assistant, an antifungal agent, anantibacterial agent, and an antioxidant may be further added to themagnetic layer. As the additives, commercially available products can besuitably selectively used according to desired properties.

The magnetic layer described above is provided on the non-magnetic layerformed on the non-magnetic support. The details of the non-magneticlayer and the non-magnetic support will be described later.

Non-Magnetic Layer

The magnetic tape includes a non-magnetic layer including non-magneticpowder and a binder between the non-magnetic support and the magneticlayer. The non-magnetic powder used in the non-magnetic layer may beinorganic powder or organic powder. In addition, carbon black and thelike can be used. Examples of the inorganic powder include powders ofmetal, metal oxide, metal carbonate, metal sulfate, metal nitride, metalcarbide, and metal sulfide. The non-magnetic powder can be purchased asa commercially available product or can be manufactured by a well-knownmethod. For details thereof, descriptions disclosed in paragraphs 0146to 0150 of JP2011-216149A can be referred to. For carbon black which canbe used in the non-magnetic layer, descriptions disclosed in paragraphs0040 and 0041 of JP2010-24113A can be referred to. The content (fillingpercentage) of the non-magnetic powder of the non-magnetic layer ispreferably in a range of 50 to 90 mass % and more preferably in a rangeof 60 to 90 mass %.

In regards to other details of a binder or additives of the non-magneticlayer, the well-known technology regarding the non-magnetic layer can beapplied. In addition, in regards to the type and the content of thebinder, and the type and the content of the additive, for example, thewell-known technology regarding the magnetic layer can be applied.

The non-magnetic layer of the invention also includes a substantiallynon-magnetic layer including a small amount of ferromagnetic powder asimpurities or intentionally, together with the non-magnetic powder.Here, the substantially non-magnetic layer is a layer having a residualmagnetic flux density equal to or smaller than 10 mT, a layer havingcoercivity equal to or smaller than 7.96 kAm (100 Oe), or a layer havinga residual magnetic flux density equal to or smaller than 10 mT andcoercivity equal to or smaller than 7.96 kAm (100 Oe). It is preferablethat the non-magnetic layer does not have a residual magnetic fluxdensity and coercivity.

Back Coating Layer

The magnetic tape can also include a back coating layer includingnon-magnetic powder and a binder on a side of the non-magnetic supportopposite to the side including the magnetic layer. The back coatinglayer preferably includes any one or both of carbon black and inorganicpowder. In regards to the binder included in the back coating layer andvarious additives which can be arbitrarily included in the back coatinglayer, a well-known technology regarding the treatment of the magneticlayer and/or the non-magnetic layer can be applied.

Non-Magnetic Support

Next, the non-magnetic support will be described. As the non-magneticsupport (also simply referred to as a “support”), well-known componentssuch as polyethylene terephthalate, polyethylene naphthalate, polyamide,polyamide imide, aromatic polyamide subjected to biaxial stretching areused. Among these, polyethylene terephthalate, polyethylene naphthalate,and polyamide are preferable. Corona discharge, plasma treatment,easy-bonding treatment, or thermal treatment may be performed withrespect to these supports in advance.

Various Thickness

In the magnetic tape, the total thickness of the magnetic layer and thenon-magnetic layer is equal to or smaller than 0.60 μm and preferablyequal to or smaller than 0.50 μm, from a viewpoint of thinning themagnetic tape. In addition, the total thickness of the magnetic layerand the non-magnetic layer is, for example, equal to or greater than0.10 μm or equal to or greater than 0.20 μm.

In the thicknesses of the non-magnetic support and each layer of themagnetic tape, the thickness of the non-magnetic support is preferably3.00 to 4.50 μm.

A thickness of the magnetic layer can be optimized in accordance withsaturation magnetization quantity of the magnetic head used, a head gaplength, or a band of a recording signal. The thickness of the magneticlayer is normally 0.01 μm to 0.15 μm, and is preferably 0.02 μm to 0.12μm and more preferably 0.03 μm to 0.10 μm, from a viewpoint of realizingrecording at high density. The magnetic layer may be at least singlelayer, the magnetic layer may be separated into two or more layershaving different magnetic properties, and a configuration of awell-known multilayered magnetic layer can be applied. A thickness ofthe magnetic layer in a case where the magnetic layer is separated intotwo or more layers is the total thickness of the layers.

The thickness of the non-magnetic layer is, for example, 0.10 to 0.55 μmand is preferably 0.10 to 0.50 μm.

A thickness of the back coating layer is preferably equal to or smallerthan 0.90 μm and even more preferably in a range of 0.10 to 0.70 μm.

In addition, the total thickness of the magnetic tape is preferablyequal to or smaller than 6.00 μm, more preferably equal to or smallerthan 5.70 μm, and even more preferably equal to or smaller than 5.50 μm,from a viewpoint of improving recording capacity for 1 magnetic tapecartridge. Meanwhile, the total thickness of the magnetic tape ispreferably equal to or greater than 1.00 μm, from a viewpoint ofavailability (handling properties) of the magnetic tape.

The thicknesses of various layers of the magnetic tape and thenon-magnetic support can be acquired by a well-known film thicknessmeasurement method. As an example, a cross section of the magnetic tapein a thickness direction is, for example, exposed by a well-known methodof ion beams or microtome, and the exposed cross section is observedwith a scan electron microscope. In the cross section observation,various thicknesses can be acquired as a thickness acquired at oneposition of the cross section in the thickness direction, or anarithmetical mean of thicknesses acquired at a plurality of positions oftwo or more positions, for example, two positions which are arbitrarilyextracted. In addition, the thickness of each layer may be acquired as adesigned thickness calculated according to the manufacturing conditions.

Measurement Method

Manufacturing of Magnetic Tape in which Servo Pattern is Formed

Preparation of Each Layer Forming Composition

Each composition for forming the magnetic layer, the non-magnetic layer,or the back coating layer which is arbitrarily provided normallyincludes a solvent, together with various components described above. Asthe solvent, organic solvents generally used for manufacturing a coatingtype magnetic recording medium can be used. Among those, from aviewpoint of solubility of the binder normally used in the coating typemagnetic recording medium, the each layer forming composition preferablyincludes one or more ketone solvents such as acetone, methyl ethylketone, methyl isobutyl ketone, diisobutyl ketone, cyclohexanone,isophorone, and tetrahydrofuran. The amount of the solvent of the eachlayer forming composition is not particularly limited, and can be set tobe the same as that of the each layer forming composition of a typicalcoating type magnetic recording medium. The steps of preparing thecomposition for forming each layer generally include at least a kneadingstep, a dispersing step, and a mixing step provided before and afterthese steps, if necessary. Each step may be divided into two or morestages. All of raw materials used in the invention may be added at aninitial stage or in a middle stage of each step. In addition, each rawmaterial may be separately added in two or more steps. For example, thebinder may be separately added in the kneading step, the dispersingstep, and a mixing step for viscosity adjustment after the dispersion.In the manufacturing step of the magnetic tape, a well-knownmanufacturing technology of the related art can be used as a part of thestep. In the kneading step, an open kneader, a continuous kneader, apressure kneader, or a kneader having a strong kneading force such as anextruder is preferably used. The details of the kneading processes ofthese kneaders are disclosed in JP1989-106338A (JP-H01-106338A) andJP1989-79274A (JP-H01-79274A). In addition, in order to disperse eachlayer forming composition, glass beads and/or other beads can be used.As such dispersion beads, zirconia beads, titania beads, and steel beadswhich are dispersion beads having high specific gravity are suitable.These dispersion beads are preferably used by optimizing a bead diameterand a filling percentage. As a dispersion device, a well-knowndispersion device can be used.

Coating Step

The magnetic layer can be formed by performing multilayer coating of themagnetic layer forming composition with the non-magnetic layer formingcomposition in order or at the same time. The back coating layer can beformed by applying the back coating layer forming composition to a sideof the non-magnetic support opposite to a side provided with themagnetic layer (or to be provided with the magnetic layer). For detailsof the coating for forming each layer, a description disclosed in aparagraph 0066 of JP2010-231843A can be referred to.

Other Steps

For details of various other steps for manufacturing the magnetic tape,descriptions disclosed in paragraphs 0067 to 0070 of JP2010-231843A canbe referred to.

One Aspect of Preferred Manufacturing Method

As a preferred manufacturing method, a manufacturing method of applyingvibration to the magnetic layer can be used, in order to improveuniformity of the thickness of the liquid film formed on the surface ofthe magnetic layer by fatty acid ester. The inventors have surmisedthat, by adding vibration, the liquid film formed on the surface of themagnetic layer by fatty acid ester flows and the uniformity of thethickness of the liquid film is improved.

That is, the magnetic tape can be manufactured by a manufacturing methodof forming the magnetic layer by applying and drying the magnetic layerforming composition including ferromagnetic powder, a binder, and fattyacid ester with the non-magnetic layer forming composition in order orat the same time, and applying vibration to the formed magnetic layer.The manufacturing method is identical to the typical manufacturingmethod of the magnetic tape, except for applying vibration to themagnetic layer, and the details thereof are as described above.

Means for applying vibration are not particularly limited. For example,the vibration can be applied to the magnetic layer, by bringing thesurface of the non-magnetic support, provided with the magnetic layerformed, on a side opposite to the magnetic layer to come into contactwith a vibration imparting unit. The non-magnetic support, provided withthe magnetic layer formed, may run while coming into contact with avibration imparting unit. The vibration imparting unit, for example,includes an ultrasonic vibrator therein, and accordingly, vibration canbe applied to a product coming into contact with the unit. It ispossible to adjust the vibration applied to the magnetic layer by avibration frequency, and strength of the ultrasonic vibrator, and/or thecontact time with the vibration imparting unit. For example, the contacttime can be adjusted by a running speed of the non-magnetic support,provided with the magnetic layer formed, while coming into contact withthe vibration imparting unit. The vibration imparting conditions are notparticularly limited, and may be set so as to control the spacingdistribution, particularly, the spacing distribution FWHM_(before)before vacuum heating. In order to set the vibration impartingconditions, a preliminary experiment can be performed before the actualmanufacturing, and the conditions can be optimized.

In addition, the spacing distribution FWHM_(after) after the vacuumheating tends to be decreased, when the dispersion conditions of themagnetic layer forming composition are reinforced (for example, thenumber of times of the dispersion is increased, the dispersion time isextended, and the like), and/or the filtering conditions are reinforced(for example, a filter having a small hole diameter is used as a filterused in the filtering, the number of times of the filtering isincreased, and the like). The inventors have surmised that this isbecause the uniformity of the height of the projection present on thesurface of the magnetic layer is improved, by improving dispersibilityand/or the uniformity of the particle size of the particulate matterincluded in the magnetic layer forming composition, particularly, thenon-magnetic filler which may function as the projection formation agentdescribed above. A preliminary experiment can be performed before theactual manufacturing, and the dispersion conditions and/or the filteringconditions can be optimized.

In addition, in the magnetic tape including the magnetic layer includingcarbon black as the non-magnetic filler, it is effect to use thedispersing agent for improving dispersibility of the carbon black as amagnetic layer component, in order to decrease the spacing distributionFWHM_(after) after the vacuum heating. For example, organic tertiaryamine can be used as a dispersing agent of carbon black. For details ofthe organic tertiary amine, descriptions disclosed in paragraphs 0011 to0018 and 0021 of JP2013-049832A can be referred to. The organic tertiaryamine is more preferably trialkylamine. An alkyl group included intrialkylamine is preferably an alkyl group having 1 to 18 carbon atoms.Three alkyl groups included in trialkylamine may be the same as eachother or different from each other. For details of the alkyl group,descriptions disclosed in paragraphs 0015 to 0016 of JP2013-049832A canbe referred to. As trialkylamine, trioctylamine is particularlypreferable.

Hereinabove, an aspect of the preferred manufacturing method has beendescribed. However, the magnetic tape according to one aspect of theinvention is not limited to a magnetic tape manufactured by themanufacturing method described above.

Formation of Servo Pattern

The magnetic tape includes a timing-based servo pattern in the magneticlayer. FIG. 1 shows a disposition example of a region (servo band) inwhich the timing-based servo pattern is formed and a region (data band)interposed between two servo bands. FIG. 2 shows a disposition exampleof the timing-based servo patterns. Here, the disposition example shownin each drawing is merely an example, and the servo pattern, the servobands, and the data bands may be disposed in the disposition accordingto a system of the magnetic tape device (drive). In addition, for theshape and the disposition of the timing-based servo pattern, awell-known technology such as disposition examples shown in FIG. 4, FIG.5, FIG. 6, FIG. 9, FIG. 17, and FIG. 20 of U.S. Pat. No. 5,689,384A canbe applied without any limitation, for example.

The servo pattern can be formed by magnetizing a specific region of themagnetic layer by a servo write head mounted on a servo writer. A regionto be magnetized by the servo write head (position where the servopattern is formed) is determined by standards. As the servo writer, acommercially available servo writer or a servo writer having awell-known configuration can be used. For the configuration of the servowriter, well-known technologies such as technologies disclosed inJP2011-175687A, U.S. Pat. No. 5,689,384A, and U.S. Pat. No. 6,542,325Bcan be referred to without any limitation.

The magnetic tape according to one aspect of the invention describedabove is a magnetic tape in which the total thickness of a non-magneticlayer and a magnetic layer is equal to or smaller than 0.60 m and servopatterns are formed in the magnetic layer, and can prevent the outputdecrease of the servo signal of the timing-based servo system.

Magnetic Tape Device

One aspect of the invention relates to a magnetic tape device includingthe magnetic tape, a magnetic head, and a servo head.

The details of the magnetic tape mounted on the magnetic tape device areas described above. The magnetic tape is generally accommodated in amagnetic tape cartridge and the magnetic tape cartridge is attached tothe magnetic tape device. Details of the structure of the magnetic tapecartridge are well known. The magnetic tape cartridge is mounted on themagnetic tape device. The magnetic tape includes timing-based servopatterns. Accordingly, a magnetic signal is recorded on the data band bythe magnetic head to form a data track, and/or, when reproducing therecorded signal, a head tracking of a timing-based servo type can beperformed based on the read servo pattern, while reading the servopattern by the servo head. Here, when the output of the servo signal isdecreased, the head positioning accuracy may be decreased, as describedabove. With respect to this, according to the magnetic tape, it ispossible to prevent the output decrease of the servo signal, andaccordingly, it is possible to cause the magnetic head to follow thedata track at a high accuracy in the timing-based servo system.

As the magnetic head mounted on the magnetic tape device, a well-knownmagnetic head which can perform the recording and/or reproducing of themagnetic signal with respect to the magnetic tape can be used. Arecording head and a reproduction head may be one magnetic head or maybe separated magnetic heads. As the servo head, a well-known servo headwhich can read the timing-based servo pattern of the magnetic tape canbe used. At least one or two or more servo heads may be included in themagnetic tape device.

For details of the head tracking of the timing-based servo system, forexample, well-known technologies such as technologies disclosed in U.S.Pat. No. 5,689,384A, U.S. Pat. No. 6,542,325B, and U.S. Pat. No.7,876,521B can be used without any limitation.

A commercially available magnetic tape device generally includes amagnetic head and a servo head in accordance to a standard. In addition,a commercially available magnetic tape device generally has a servocontrolling mechanism for realizing head tracking of the timing-basedservo system in accordance to a standard. The magnetic tape deviceaccording to one aspect of the invention can be configured byincorporating the magnetic tape according to one aspect of the inventionto a commercially available magnetic tape device.

EXAMPLES

Hereinafter, the invention will be described with reference to Examples.However, the invention is not limited to aspects shown in the Examples.“Parts” in the following description means “parts by mass”, unlessotherwise noted.

Example 1

Magnetic Layer Forming Composition

Magnetic Solution

Ferromagnetic hexagonal ferrite powder: 100.0 parts

(coercivity Hec: 2100 Oe (168 kA/m), average particle size: 25 nm)

Sulfonic acid group-containing polyurethane resin: 15.0 parts

Cyclohexanone: 150.0 parts

Methyl ethyl ketone: 150.0 parts

Abrasive Liquid

α-alumina (average particle size of 110 nm): 9.0 parts

Vinyl chloride copolymer: (MR110 manufactured by Zeon Corporation): 0.7parts

Cyclohexanone: 20.0 parts

Silica Sol

Colloidal silica prepared by a sol-gel method (average particle size:120 nm): 3.5 parts

Methyl ethyl ketone: 8.2 parts

Other Components

Butyl stearate: 1.0 part

Stearic acid: 1.0 part

Polyisocyanate (CORONATE manufactured by Nippon Polyurethane Industry):2.5 parts

Finishing Additive Solvent

Cyclohexanone: 180.0 parts

Methyl ethyl ketone: 180.0 parts

Non-Magnetic Layer Forming Composition

Non-magnetic inorganic powder (α-iron oxide): 80.0 parts

(average particle size: 0.15 μm, average acicular ratio: 7,Brunauer-Emmett-Teller (BET) specific surface area: 52 m²/g)

Carbon black (average particle size of 20 nm): 20.0 parts

Electron beam-curable vinyl chloride copolymer: 13.0 parts

Electron beam-curable polyurethane resin: 6.0 parts

Phenylphosphonic acid: 3.0 parts

Cyclohexanone: 140.0 parts

Methyl ethyl ketone: 170.0 parts

Butyl stearate: see Table 1

Stearic acid: see Table 1

Back Coating Layer Forming Composition

Non-magnetic inorganic powder (α-iron oxide): 80.0 parts

(average particle size: 0.15 μm, average acicular ratio: 7, BET specificsurface area: 52 m²/g)

Carbon black (average particle size of 20 nm): 20.0 parts

Carbon black (average particle size of 100 nm): 3.0 parts

Vinyl chloride copolymer: 13.0 parts

Sulfonic acid group-containing polyurethane resin: 6.0 parts

Phenylphosphonic acid: 3.0 parts

Cyclohexanone: 140.0 parts

Methyl ethyl ketone: 170.0 parts

Stearic acid: 3.0 parts

Polyisocyanate (CORONATE manufactured by Nippon Polyurethane Industry):5.0 parts

Methyl ethyl ketone: 400.0 parts

Preparation of Each Layer Forming Composition

The magnetic layer forming composition was prepared by the followingmethod.

The magnetic solution was kneaded and diluted by an open kneader, andsubjected to a dispersing process of 12 passes, with a transverse beadsmill dispersion device and zirconia (ZrO₂) beads (hereinafter, referredto as “Zr beads”) having a bead diameter of 0.5 mm, by setting a beadfilling percentage as 80 volume %, a circumferential speed of rotor tipas 10 m/sec, and a retention time for 1 pass as 2 minutes.

After mixing the components described above, the abrasive solution wasput in a vertical sand mill dispersion device together with Zr beadshaving a bead diameter of 1 mm, the bead volume/(abrasive solutionvolume+bead volume) was adjusted to be 60%, the sand mill dispersingprocess was performed for 180 minutes, a solution after the process isextracted, and an ultrasonic dispersion filtering process was performedwith a flow-type ultrasonic dispersion filtering device.

The magnetic solution, the silica sol, the abrasive solution, othercomponents, and the finishing additive solvent are introduced into adissolver stirring device, and were stirred at a circumferential speedof 10 m/sec for 30 minutes. After that, the treatment is performed witha flow-type ultrasonic dispersion device at a flow rate of 7.5 kg/minfor the number of times of the passes shown Table 1, and then, amagnetic layer forming composition was prepared by performing filteringwith a filter having a hole diameter shown in Table 1, for the number oftimes of the passes shown Table 1.

The non-magnetic layer forming composition was prepared by the followingmethod. Each component excluding a lubricant (butyl stearate and stearicacid) was kneaded with an open kneader and diluted, and then, wasdispersed by using a horizontal bead mill dispersion device. After that,the lubricant (butyl stearate and stearic acid) was added thereto, andstirred and mixed with a dissolver stirring device, to prepare anon-magnetic layer forming composition.

The back coating layer forming composition was prepared by the followingmethod. Each component excluding the lubricant (stearic acid),polyisocyanate, and methyl ethyl ketone (400.0 parts) was kneaded withan open kneader and diluted, and then, was dispersed by using ahorizontal bead mill dispersion device. After that, the lubricant(stearic acid), polyisocyanate, and methyl ethyl ketone (400.0 parts)were added thereto, and stirred and mixed with a dissolver stirringdevice, to prepare a back coating layer forming composition.

Manufacturing of Magnetic Tape

The non-magnetic layer forming composition was applied onto apolyethylene naphthalate support having a thickness shown in Table 1 anddried so that the thickness after the drying becomes the thickness shownin Table 1, and then, an electron beam was emitted with an energy of 40kGy at an acceleration voltage of 125 kV. The magnetic layer formingcomposition was applied thereto and dried so that the thickness afterthe drying becomes the thickness shown in Table 1, to form a coatinglayer of the magnetic layer forming composition.

After that, the support, provided with the coating layer formed, wasinstalled in a vibration imparting device shown in FIG. 3 so that thesurface thereof on a side opposite to the surface where the coatinglayer is formed comes into contact with the vibration imparting unit,and the support (in FIG. 3, reference numeral 101), provided with thecoating layer formed, was transported at a transportation speed of 0.5m/sec, to apply vibration to the coating layer. In FIG. 3, a referencenumeral 102 denotes a guide roller (a reference numeral 102 denotes oneof two guide rollers), a reference numeral 103 denotes the vibrationimparting device (vibration imparting unit including the ultrasonicvibrator), and an arrow denotes a transportation direction. The timefrom the start of the contact of the arbitrary portion of the support,provided with the coating layer formed, with the vibration impartingunit until the end of the contact is shown in Table 1 as the vibrationimparting time. The vibration imparting unit used includes an ultrasonicvibrator therein. The vibration was imparted by setting a vibrationfrequency and the intensity of the ultrasonic vibrator as values shownin Table 1.

After that, the back coating layer forming composition was applied ontothe surface of the support on a side opposite to the surface where thenon-magnetic layer and the magnetic layer are formed, and dried so thatthe thickness after the drying becomes thickness shown in Table 1. Afterthat, the surface smoothing treatment (calender process) was performedwith a calender roll configured of only a metal roll, at a calenderprocess speed of 80 m/min, linear pressure of 300 kg/cm (294 kN/m), anda surface temperature of a calender roll of 95° C.

Then, the thermal treatment was performed in the environment of theatmosphere temperature of 70° C. for 36 hours. After the thermaltreatment, the slitting was performed so as to have a width of ½ inches(0.0127 meters), and the surface of the magnetic layer was cleaned witha tape cleaning device in which a nonwoven fabric and a razor blade areattached to a device including a sending and winding devices of the slitso as to press the surface of the magnetic layer.

By doing so, the magnetic tape was manufactured.

Formation of Timing-Based Servo Pattern

In a state where the magnetic layer of the manufactured magnetic tapewas demagnetized, servo patterns having disposition and shapes accordingto the LTO Ultrium format were formed on the magnetic layer by using aservo write head mounted on a servo testing machine. Accordingly, amagnetic tape including data bands, servo bands, and guide bands in thedisposition according to the LTO Ultrium format in the magnetic layer,and including servo patterns having the disposition and the shapeaccording to the LTO Ultrium format on the servo band is obtained. Inthis magnetic tape, total 5,000,000 servo frames of servo framesincluding the A burst, B burst, C burst, and D burst are formed in thedisposition shown in FIG. 2. The servo testing machine includes a servowrite head and a servo head. This servo testing machine was also used inthe evaluation which will be described later.

Examples 2 to 5 and Comparative Examples 1 to 9

A magnetic tape was manufactured in the same manner as in Example 1,except for changing the list of the non-magnetic layer formingcomposition and/or the manufacturing conditions shown in Table 1. Thevibration imparting time was adjusted by changing the transportationspeed of the support, provided with the coating layer formed, of themagnetic layer forming composition.

In the magnetic tape of Comparative Example 7 and the magnetic tape ofComparative Example 8, the following evaluation was performed regardingthe magnetic tape in a state before forming a servo pattern. This isbecause of the following reasons.

When the servo pattern was formed in the magnetic tape of ComparativeExample 7 by the same method as in Example 1, the running of themagnetic tape was difficult due to the occurrence of sticking betweenthe servo write head and the surface of the magnetic layer, while thesurface of the magnetic layer of the running magnetic tape comes intocontact with and slide on the servo write head. Accordingly, theformation of the servo pattern was stopped.

In addition, when the servo pattern was formed in the magnetic tape ofComparative Example 8 by the same method as in Example 1, the running ofthe magnetic tape was difficult due to an effect of the attachedmaterial attached to the servo write head, while the surface of themagnetic layer of the running magnetic tape comes into contact with andslide on the servo write head. Accordingly, the formation of the servopattern was stopped. After the formation of the servo pattern wasstopped, the surface of the magnetic layer of the magnetic tape ofComparative Example 8 was observed with an optical microscope, andscratches were confirmed. Therefore, the attached materials may be cutscrap generated due to the cutting of the surface of the magnetic layerdue to the contact with the servo write head.

The thickness of each layer and the non-magnetic support of the magnetictape manufactured was acquired by the following method. It was confirmedthat the thickness of each layer and the non-magnetic support formed isthe thickness shown in Table 1.

The cross section of the magnetic tape in a thickness direction wasexposed by an ion beam, and then, the cross section observation of theexposed cross section was performed with a scanning electron microscope.Various thicknesses were acquired as an arithmetical mean of thicknessesacquired at two positions in the thickness direction, in the crosssection observation.

Physical Properties Evaluation Method of Magnetic Tape

1. Spacing Distributions FWHM_(before) and FWHM_(after) Before and afterVacuum Heating

The spacing distributions FWHM_(before) and FWHM_(after) before andafter vacuum heating were acquired by the following method by using atape spacing analyzer (TSA) (manufactured by MicroPhysics, Inc.).

In a state where a glass sheet included in the TSA was disposed on thesurface of the magnetic layer of the magnetic tape, a hemisphere waspressed against the surface of the back coating layer of the magnetictape at pressure of 5.05×10⁴ N/m (0.5 atm) by using a hemisphere made ofurethane included in the TSA as a pressing member. In this state, agiven region (150,000 to 200,000 μm²) of the surface of the magneticlayer of the magnetic tape was irradiated with white light from astroboscope included in the TSA through the glass sheet, and theobtained reflected light was received by a charge-coupled device (CCD)through an interference filter (filter selectively passing light at awavelength of 633 nm), and thus, an interference fringe image generatedon the uneven part of the region was obtained.

This image was divided into 300,000 points, a distance (spacing) betweenthe surface of the glass sheet on the magnetic tape side and the surfaceof the magnetic layer of the magnetic tape was acquired, and the fullwidth at half maximum of spacing distribution was full width at halfmaximum, when this spacing was shown with a histogram, and thishistogram was fit with Gaussian distribution.

The vacuum heating was performed by storing the magnetic tape in avacuum constant temperature drying machine with a degree of vacuum of200 Pa to 0.01 Mpa and at inner atmosphere temperature of 70° C. to 90°C. for 24 hours.

2. Difference (S_(after)−S_(before))

The difference (S_(after)−S_(before)) was a value obtained bysubtracting a mode of the histogram before the vacuum heating from amode of the histogram after the vacuum heating obtained in the section1.

Performance Evaluation Method of Magnetic Tape

Output Decreased Amount of Servo Signal

The magnetic tape in which the timing-based servo pattern is formed wasattached to a servo testing machine. In the servo testing machine, theservo patterns were sequentially read (servo signals were reproduced) bythe servo head from the servo pattern of the first servo frame formed inthe magnetic tape to the servo pattern of the final 5,000,000-th servoframe, while bringing the surface of the magnetic layer of the runningmagnetic tape to come into contact with and slide on the servo head. Anarithmetical mean of the signal output obtained in the first to 100-thservo frames was set as A, an arithmetical mean of the signal outputobtained in the 4,999,900-th to 5,000,000-th servo frames was set as B,and the output decreased amount of the servo signal (unit: %) wascalculated with an expression of “[(B−A)/A]×100”.

The results described above are shown in Table 1.

TABLE 1 Comparative Comparative Comparative Comparative ComparativeComparative Comparative Unit Example 1 Example 2 Example 3 Example 4Example 5 Example 6 Example 7 Non- Butyl stearate Content Part 4.0 4.04.0 4.0 8.0 4.0 10.0 magnetic Stearic acid Content Part 1.0 1.0 1.0 1.01.0 1.0 1.0 layer forming compo- sition Manu- Ultrasonic ImpartingSecond None None None None None 0.5 0.5 facturing vibration timeconditions imparting Frequency kHz 30 30 conditions Intensity W 100 100Magnetic layer Number of Times 2 2 2 2 2 1 2 forming times ofcomposition passes of preparation flow-type conditions ultrasonicdispersion device Number of Times 1 1 1 1 1 1 1 times of filteringFilter hole μm 1.0 1.0 1.0 1.0 1.0 1.0 1.0 diameter Physical Magneticlayer Thickness μm 0.10 0.10 0.10 0.10 0.10 0.10 0.10 propertiesNon-magnetic Thickness μm 1.00 0.70 0.50 0.10 0.50 0.50 0.50 layerNon-magnetic Thickness μm 4.30 4.30 4.30 4.30 4.30 4.30 4.30 supportBack coating Thickness μm 0.60 0.60 0.60 0.60 0.60 0.60 0.60 layerNon-magnetic Total μm 1.10 0.80 0.60 0.20 0.60 0.60 0.60 layer +thickness magnetic layer Safter-Sbefore nm 6.0 4.2 3.2 1.0 6.0 3.1 8.2FWHMbefore nm 8.7 8.8 8.5 8.6 8.6 6.8 6.9 FWHMafter nm 6.9 6.8 7.0 7.06.8 7.5 6.9 Perfor- Servo signal output % −0.2 −0.9 −6.3 −16.0 −4.5 −6.0— mance decrease Comparative Comparative Unit Example 8 Example 9Example 1 Example 2 Example 3 Example 4 Example 5 Non-magnetic Butylstearate Content Part 0.0 4.0 4.0 4.0 2.0 8.0 4.0 layer forming Stearicacid Content Part 1.0 2.0 1.0 1.0 1.0 1.0 1.0 composition ManufacturingUltrasonic Imparting Second 0.5 None 0.5 3.0 0.5 0.5 3.0 conditionsvibration time imparting Frequency kHz 30 30 30 30 30 30 conditionsIntensity W 100 100 100 100 100 100 Magnetic layer Number of Times 2 2 230 2 2 30 forming times of composition passes of preparation flow-typeconditions ultrasonic dispersion device Number of Times 1 1 1 5 1 1 5times of filtering Filter hole μm 1.0 1.0 1.0 0.5 1.0 1.0 0.5 diameterPhysical Magnetic layer Thickness μm 0.10 0.10 0.10 0.10 0.10 0.10 0.10properties Non-magnetic Thickness μm 0.50 0.50 0.50 0.50 0.50 0.50 0.10layer Non-magnetic Thickness μm 4.30 4.30 4.30 4.30 4.30 4.30 4.30support Back coating Thickness μm 0.60 0.60 0.60 0.60 0.60 0.60 0.60layer Non-magnetic Total μm 0.60 0.60 0.60 0.60 0.60 0.60 0.20 layer +thickness magnetic layer Safter-Sbefore nm 0 3.2 3.1 2.9 1.5 6.2 3.1FWHMbefore nm 6.8 8.5 6.8 4.1 7.0 4.1 3.9 FWHMafter nm 7.0 7.0 6.9 4.06.9 3.9 4.0 Performance Servo signal output % — −6.2 −0.3 0.0 −0.8 −0.2−0.1 decrease

With the comparison of Comparative Examples, it was confirmed that, inthe case where the total thickness of the non-magnetic layer and themagnetic layer is equal to or smaller than 0.60 μm (Comparative Examples3 to 6 and 9), the output of the servo signal is significantlydecreased, compared to the case where the total thickness of thenon-magnetic layer and the magnetic layer exceeds 0.60 μm (ComparativeExamples 1 and 2).

With respect to this, in the magnetic tape of Examples 1 to 5, the totalthickness of the non-magnetic layer and the magnetic layer is equal toor smaller than 0.60 μm, however, the output decrease of the servosignal was prevented, compared to that of the magnetic tape ofComparative Examples 3 to 6 and 9.

An aspect of the invention can be effective in technical fields ofmagnetic tapes for high-density recording.

What is claimed is:
 1. A magnetic tape comprising: a non-magneticsupport; a non-magnetic layer including non-magnetic powder and a binderon the non-magnetic support; and a magnetic layer includingferromagnetic powder and a binder on the non-magnetic layer, wherein thetotal thickness of the non-magnetic layer and the magnetic layer isequal to or smaller than 0.60 m, the magnetic layer includes atiming-based servo pattern, the magnetic layer includes fatty acidester, a full width at half maximum of spacing distribution measured byoptical interferometry regarding the surface of the magnetic layerbefore performing vacuum heating with respect to the magnetic tape isgreater than 0 nm and equal to or smaller than 7.0 nm, a full width athalf maximum of spacing distribution measured by optical interferometryregarding the surface of the magnetic layer after performing the vacuumheating with respect to the magnetic tape is greater than 0 nm and equalto or smaller than 7.0 nm, and a difference S_(after)−S_(before) betweena spacing S_(after) measured by optical interferometry regarding thesurface of the magnetic layer after performing the vacuum heating withrespect to the magnetic tape and a spacing S_(before) measured byoptical interferometry regarding the surface of the magnetic layerbefore performing the vacuum heating with respect to the magnetic tapeis greater than 0 nm and equal to or smaller than 8.0 nm.
 2. Themagnetic tape according to claim 1, wherein the total thickness of thenon-magnetic layer and the magnetic layer is 0.20 μm to 0.60 μm.
 3. Themagnetic tape according to claim 1, wherein the differenceS_(after)−S_(before) is greater than 0 nm and equal to or smaller than7.0 nm.
 4. The magnetic tape according to claim 1, wherein thedifference S_(after)−S_(before) is 2.0 nm to 7.0 nm.
 5. The magnetictape according to claim 1, wherein the full width at half maximum ofspacing distribution measured by optical interferometry regarding thesurface of the magnetic layer before performing vacuum heating withrespect to the magnetic tape is greater than 0 nm and equal to orsmaller than 5.0 nm.
 6. The magnetic tape according to claim 1, whereinthe full width at half maximum of spacing distribution measured byoptical interferometry regarding the surface of the magnetic layer afterperforming the vacuum heating with respect to the magnetic tape isgreater than 0 nm and equal to or smaller than 5.0 nm.
 7. The magnetictape according to claim 1, wherein the magnetic layer includes anon-magnetic filler.
 8. The magnetic tape according to claim 7, whereinthe non-magnetic filler is colloidal particles.
 9. The magnetic tapeaccording to claim 8, wherein colloidal particles are silica colloidalparticles.
 10. A magnetic tape device comprising: a magnetic tape; amagnetic head; and a servo head, wherein the magnetic tape is a magnetictape comprising: a non-magnetic support; a non-magnetic layer includingnon-magnetic powder and a binder on the non-magnetic support; and amagnetic layer including ferromagnetic powder and a binder on thenon-magnetic layer, wherein the total thickness of the non-magneticlayer and the magnetic layer is equal to or smaller than 0.60 m, themagnetic layer includes a timing-based servo pattern, the magnetic layerincludes fatty acid ester, a full width at half maximum of spacingdistribution measured by optical interferometry regarding the surface ofthe magnetic layer before performing vacuum heating with respect to themagnetic tape is greater than 0 nm and equal to or smaller than 7.0 nm,a full width at half maximum of spacing distribution measured by opticalinterferometry regarding the surface of the magnetic layer afterperforming the vacuum heating with respect to the magnetic tape isgreater than 0 nm and equal to or smaller than 7.0 nm, and a differenceS_(after)−S_(before) between a spacing S_(after) measured by opticalinterferometry regarding the surface of the magnetic layer afterperforming the vacuum heating with respect to the magnetic tape and aspacing S_(before) measured by optical interferometry regarding thesurface of the magnetic layer before performing the vacuum heating withrespect to the magnetic tape is greater than 0 nm and equal to orsmaller than 8.0 nm.
 11. The magnetic tape device according to claim 10,wherein the total thickness of the non-magnetic layer and the magneticlayer of the magnetic tape is 0.20 μm to 0.60 μm.
 12. The magnetic tapedevice according to claim 10, wherein the differenceS_(after)−S_(before) is greater than 0 nm and equal to or smaller than7.0 nm.
 13. The magnetic tape device according to claim 10, wherein thedifference S_(after)−S_(before) is 2.0 nm to 7.0 nm.
 14. The magnetictape device according to claim 10, wherein the full width at halfmaximum of spacing distribution measured by optical interferometryregarding the surface of the magnetic layer before performing vacuumheating with respect to the magnetic tape is greater than 0 nm and equalto or smaller than 5.0 nm.
 15. The magnetic tape device according toclaim 10, wherein the full width at half maximum of spacing distributionmeasured by optical interferometry regarding the surface of the magneticlayer after performing the vacuum heating with respect to the magnetictape is greater than 0 nm and equal to or smaller than 5.0 nm.
 16. Themagnetic tape device according to claim 10, wherein the magnetic layerincludes a non-magnetic filler.
 17. The magnetic tape device accordingto claim 16, wherein the non-magnetic filler is colloidal particles. 18.The magnetic tape device according to claim 17, wherein colloidalparticles are silica colloidal particles.